Sikaflex-515 white RAPIDO UNIVERS 300 ml

€11.90
VAT included
11.9

Rif: 6768

Sikaflex-515 white

Single-layer sealant based on Sika's Silane Terminated Polymer (STP) technology. Free from isocyanate. Suitable for all thermoformed, fiberglass, aluminum, etc.

It hardens on exposure to atmospheric moisture forming a resistant elastomer.

Excellent sealing properties; for interiors but also for exteriors.

Suitable for most sealing applications, it bonds well all materials such as metals, ABS, PC, fiberglass and wood.

  • Rapid film formation
  • Good resistance to atmospheric agents and good thermal stability
  • Adheres to a wide range of substrates
  • Elastic and excellent workability
  • Overpaintable
  • Low odor level
  • VOC solvent free
  • Free from PVC silicone
Quantity
Out-of-Stock

  DISCOUNT - MAKE A PURCHASE OF AT LEAST €200

You will immediately get a €10 discount

  ITALY - SHIPPING POLICIES

Shipping starting from € 8.90 up to 2 kg and not bulky (sum three sides not exceeding one meter)

  EUROPE - SHIPPING POLICIES

Shipping from €22.00 up to 2 kg and not bulky (sum 3 sides over a meter). Superiors ask quote.

  UK - MINIMUM ORDER £135

Orders minimum £135, excluding shipping. Customs duties and taxes are the customer's responsibility.

Compliant with ISO 9001/14001 standards

Fields of application

Sikaflex® -515 is a universal sealant suitable for most sealing applications in the industrial construction of commercial vehicles.

The product is characterized by excellent sealing properties for both indoors and outdoors.

It well bonds all materials commonly used in the commercial vehicle industry, such as metals, ABS, PC, fiberglass and wood.

This product is intended for use by professional users.

Preliminary checks with substrates and specific application conditions are recommended to ensure perfect adhesion and material compatibility.

Typical Product Data

  • Chemical basis Silane terminated polymer Color (CQP1 001-1)
  • Curing mechanism Atmospheric humidity
  • Density (uncured) depends on the color 1.48 kg / l
  • Non-slip properties (thixotropy)
  • Good Ambient application temperature 5 - 40 ° C
  • Dust-free time2) (CQP 019-1) 25 min
  • Open time2) (CQP 526-1) 20 min
  • Hardening speed (CQP 049-1) see diagram 1
  • Volumetric shrinkage (CQP 014-1) 3%
  • Shore A hardness (CQP 023-1 / ISO 868) 25
  • Tensile strength (CQP 036-1 / ISO 37) 1.1 MPa
  • Elongation at break (CQP 036-1 / ISO 37) 300%
  • Tear resistance (CQP 045-1 / ISO 34) 5.0 N / mm
  • Glass transition temperature (CQP 509-1 / ISO 4663) -50 ° C
  • Serving temperature (CQP 513-1) 4 hours 90 ° C 120 ° C
  • Stability (stored at T

Hardening mechanism

Sikaflex® -515 hardens by reaction with atmospheric moisture.

At low temperatures the aqueous percentage of the air is lower and hardening proceeds more slowly (see diagram).

If Sikaflex® -515 is used in combination with a polyurethane adhesive, the latter must be fully cured before sealing with Sikaflex® -515.

6768